Novatio MFL-2480 2K Metal Filler - cartridge 195ml

2-COMPONENT METAL REPAIR

MFL-2480 2K Metal Filler is a lead-free alternative to tin solder when repairing all steel and aluminium surfaces. Thanks to the low-temperature processing, deformation of the sheet material is avoided.

Fast-curing 2-component epoxy with good workability and high filling capacity. Curing can be accelerated by heating with hot air or infrared.

After curing, it is easy to machine and forms an excellent basis for further finishing with all types of filler.

MFL-2480 2K Metal Filler offers strong corrosion protection without risk of delamination.

Advantages

Safe alternative to tin solder

Quickly sandable

Shrink-free

Strong adhesion to all metals

Use

MFL-2480 2K Metal Filler can be used with a manual, electric or pneumatic gun.

Preparation

• Roughen the material well, make it dust-free and degrease with Safety Clean.
• Then deep-clean with Multifoam and blow dry.

Use

• Cartridge preparation.
• Remove the sealing cap from the cartridge.
• Place the cartridge in the gun and pump until both components come out of the cartridge evenly.
• Place the mixer tip on the cartridge and, if necessary, cut it to the desired spray opening.
• First dispense 2,5 to 3 cm of product. This is not used.
• Apply sufficient product for the repair and spread it with a spatula. Bring it into shape as well as possible within the open time (25 minutes at 23°C).
• Let it cure for 2-3 hours at room temperature. When heating to 45°C (infrared, hot air), curing accelerates and it can be sanded after just 20 minutes.
• Clean materials and spilled product with Safety Clean and/or Nova Wipe.
• After an interruption of 10 minutes, use a new mixer tip.
• For storage: leave the mixer tip on. At the next use, change the mixer tip.

Technical specifications

• Type: 2-component epoxy.
• Colour: light grey.
• Density: 1.35 +/-0.05.
• Form: paste.
• Application temperature (substrate): +10°C /+30°C.
• Curing (23°C): mixing time: 10 minutes.
• Open working time: 25 minutes:
  • sandable 23°C: 2-3 hours
  • sandable 45°C: 20 minutes
• Hardness: shore D 80.
• Tensile strength: 34 N/mm².
• Elongation at break: 10%.
• Adhesion force (23°C, 1mm thickness):
  • cold-rolled steel (CRS): 16 N/mm²
  • stainless steel: 13 N/mm²
  • galvanised steel: 14 N/mm²
  • aluminium: 10 N/mm²
• Shelf life: Store between +15°C and +30°C. 18 months in closed packaging. A few weeks shelf life in opened packaging, with mixer tip fitted.