Novatio NPG-1370 Nova Power Grip 2K ME - cartridge 250ml

LOW-ISOCYANATE, IMPACT-RESISTANT CONSTRUCTION ADHESIVE

• Odourless, shrink-free 2-component polyurethane adhesive with an extremely low isocyanate content.
• Safe to use, no certification or training required.
• Handling strength after 30 minutes, workable and fully loadable after 1-2 hours.
• Very high adhesive strength and highly shock-resistant.
• An opened cartridge can be used several times.
• The micro-emission formulation means that users do not have to follow specific training and can work with the product without health risks.

Advantages

Bonding, filling and repairing

Handling strength after 30 minutes

Can be machined: sanding, drilling, milling, tapping,…

ME: Micro-emission, very low content of free isocyanates

Use

Surface preparation

• Make the surface dust-free.
• Sand smooth materials (grit 120).
• Degrease with Safety Clean and/or Multifoam and let dry.

Cartridge preparation

• Remove the sealing cap from the cartridge and place the cartridge in the gun. Pump until both components come out of the cartridge evenly.
• Place the mixer tip on the cartridge. Spray out the first 2 cm of product onto a piece of cardboard, do not use.

Use

• Apply evenly to or into the materials to be bonded or filled. The ideal adhesive thickness for optimal strength is 0,5-1 mm
• Filling can be done in a single layer up to +/- 10 mm. After the first curing (30 minutes) a new layer can be applied.
• After an interruption of +/- 3 minutes: fit a new mixer tip.
• Clean spilled adhesive with Safety Clean and/or novawipes
• Always carry out an adhesion test when used on difficult-to-bond materials.

Storage

• Leave the mixer tip fitted until the next use. In this way Nova Power Grip remains usable for 4-6 months.
• When reusing: remove the old mixer tip, clean the outlet openings and fit a new mixer tip.

Tips:

• Higher temperatures mean faster curing. Warm the parts and/or the Nova Power Grip cartridge up to a maximum of 50°C .
• Use Q-Fix 120 for strong anchoring in drill holes.

Technical specifications

• Base: polyurethane.
• Colour: beige
• Mixer time: 3 min.
• Working time: 6 min.
• Handleable after: 30 min.
• Fully loadable after: 90 min.
• Hardness: Shore D 70.
• Tensile strength: 2600 N/cm².
• Shear strength on aluminium (sanded): 650 N/cm².
• Shear strength on stainless steel (sanded): 910 N/cm².
• Shear strength on PVC (sanded): 270 N/cm².
• Shear strength on polycarbonate (sanded): 880 N/cm².
• Elongation at break: 58 %.
• Chemical resistance:
  • Good: water, seawater, alcohols, diluted acids and bases, aliphatic solvents, fuels, oils
  • Poor: concentrated acids and bases, acetone
• Shelf life: 24 months in original, closed packaging; store cool, dry and frost-free. After opening still usable for up to 6 months.
• Safety measures: Please consult the safety data sheet.