Novatio Seal & Bond MS62 X black - cartridge 290ml
19,85 €excl. VAT
Ihned k dispozici, dodací lhůta 1-3 Days
Informace o výrobku "Novatio Seal & Bond MS62 X black - cartridge 290ml"
HIGH-TECH CONSTRUCTION ADHESIVE
MS62 X was developed for use in all conditions: from -10°C to +40°C and where high immediate and long-term adhesion is required. MS62 X is vibration-resistant, can be overpainted and is very resistant to weathering, UV rays and chemical corrosion. This makes it excellently suited for use in all environments, from construction to industry.
Advantages
Applicable from -10°C to +40°C.
High initial adhesion and dimensionally stable.
Mould-resistant.
Ecological and safe.
Use
- Bring the cartridge to room temperature before use.
- Apply to a clean substrate, free of snow and ice, cleaning with Safety Clean and/or Multifoam if necessary. FS version if required.
Test adhesion on plastics, powder coatings, exotic wood species and bituminous materials. On difficult synthetic materials, Seal & Bond Special Primer can improve adhesion.
First reinforce weak and/or porous substrates with Fixapox.
Alkyd resin-containing paints will cure more slowly.
Use Safety Clean for a perfect finish and for removing uncured Novatio polymers.
Use Novakleen for finishing on porous materials.
Technical specifications
- Base : hybrid MS polymer.
- Odour: neutral.
- Curing: by air humidity.
- Shore-A hardness (DIN 53505): 62.
- E-modulus 100% elongation (DIN 53504 S2): +/- 1.3 N/mm².
- Tensile strength (DIN 53504 S2): +/- 2.2 N/mm².
- Elongation at break (DIN 53504 S2): +/- 350%.
- Movement capacity: 12.5%.
- Consistency (DIN EN ISO 7390) : stable up to ≤ 40 mm.
- Application temperature: -10°C to +40°C.
- Skin formation at 23°C/ 50% RH: 5-6 minutes.
- Shrinkage (DIN EN ISO 10563): ≤ 5 %.
- Overpaintable: yes (alkyd resin-based paints will cure with delay).
- Relative density: 1.4.
- Temperature resistance: -40°C to +90°C.
- Frost resistance: to -20°C during transport.
- Shelf life: 12 months, stored cool and dry in the original packaging.